Multi-material Direct Ink Writing and Embroidery for Stretchable Wearable Sensors

Textile-integrated capacitive sensors offer flexible and conformable tactile sensing for wearable electronics and human-robot interaction; however, the influence of yarn-level architecture on capacitive transduction characteristics remains insufficiently quantified. This work presents a textile capacitive sensing platform based on silver-coated yarns coated with polydimethylsiloxane and assembled into one-, two-, and four-layer twisted configurations. The influence of effective electrode overlap area and inter-fiber separation on the capacitive response is systematically investigated, enabling architecture-dependent tuning of pressure and proximity sensing characteristics. Pressure was calculated using the localized single-fiber contact area, corresponding to stresses of 0.4-3.9 MPa. Increasing the layer number improved mechanical strength and sensing performance: elongation at break increased from 37.5% to 62.5% and 85.0%, while the maximum load increased from 23.3 to 42.7 and 89.7 N. Sensitivity increased with layer number and frequency, reaching 0.1331 MPa$^{-1}$ for the four-layer sensor at 100 kHz. The four-layer configuration also exhibited low hysteresis, minimal thermal drift from 25 to 90 $^\circ$C, and stable operation over 15,000 cycles. Proximity detection ranges of 60, 50, and 40 mm were obtained for the one-, two-, and four-layer sensors, respectively, revealing an architecture-dependent sensitivity-range trade-off. A 4$\times$4 textile sensing array enabled spatial contact mapping, while robotic-arm integration demonstrated real-time touch and proximity detection with an end-to-end robotic system latency (from detection to robot reaction) of 403 ms. The results establish yarn architecture as a tunable design parameter governing the measurement characteristics of textile-integrated capacitive sensing systems.

Existing stretch and touch sensors for robots are generally expensive with respect to at least one of material costs, required manufacturing equipment, or manufacturing time. We present and experimentally characterize a conductive fiber made using only inexpensive commercial off-the-shelf parts (conductive thread at $0.07/ft, silicone tubing at$0.94/ft) and tools (loop-style needle threader at $2), which can be manufactured quickly (20 cm length in 2 minutes.) We demonstrate its use as a resistive strain sensor with three applications: Triggering a grasp in a pneumatically actuated assistive finger, sensing the pose of a pneumatically actuated robotic strap, and estimating the pose of a flexible solid. We also demonstrate that it can be used as a capacitive sensor with two applications: First, as a touch sensor which triggers a commercial robot arm to move, and second, as a near-field sensor enabling the robot arm to follow a moving hand. The capacitive sensors are knitted, showcasing the high flexibility of the fiber. We discuss methods for improving manufacturing scalability and their cost trade-offs. Finally, we demonstrate a method for repairing a cut fiber.

This work introduces Ori-Sense, a compliant capacitive sensor inspired by the inverted Kresling origami pattern. The device translates torsional deformation into measurable capacitance changes, enabling proprioceptive feedback for soft robotic systems. Using dissolvable-core molding, we fabricated a monolithic silicone structure with embedded conductive TPU electrodes, forming an integrated soft capacitor. Mechanical characterization revealed low stiffness and minimal impedance, with torque values below 0.01 N mm for axial displacements between -15 mm and 15 mm, and up to 0.03 N mm at 30 degrees twist under compression. Finite-element simulations confirmed localized stresses along fold lines and validated the measured torque-rotation response. Electrical tests showed consistent capacitance modulation up to 30%, directly correlated with the twist angle, and maximal sensitivity of S_theta ~ 0.0067 pF/deg at 5 mm of axial deformation.