Process Optimization Under Uncertainty for Improving the Bond Quality of Polymer Filaments in Fused Filament Fabrication

This work presents a data-driven methodology for multi-objective optimization under uncertainty of process parameters in the fused filament fabrication (FFF) process. The proposed approach optimizes the process parameters with the objectives of minimizing the geometric inaccuracy and maximizing the filament bond quality of the manufactured part. First, experiments are conducted to collect data pertaining to the part quality. Then, Bayesian neural network (BNN) models are constructed to predict the geometric inaccuracy and bond quality as functions of the process parameters. The BNN model captures the model uncertainty caused by the lack of knowledge about model parameters (neuron weights) and the input variability due to the intrinsic randomness in the input parameters. Using the stochastic predictions from these models, different robustness-based design optimization formulations are investigated, wherein process parameters such as nozzle temperature, nozzle speed, and layer thickness are optimized under uncertainty for different multi-objective scenarios. Epistemic uncertainty in the prediction model and the aleatory uncertainty in the input is considered in the optimization. Finally, Pareto surfaces are constructed to estimate the tradeoffs between the objectives. Both the BNN models and the effectiveness of the proposed optimization methodology are validated using the actual manufacturing of the parts.

This article investigates several physics-informed and hybrid machine learning strategies that incorporate physics knowledge in experimental data-driven deep-learning models for predicting the bond quality and porosity of fused filament fabrication (FFF) parts. Three types of strategies are explored to incorporate physics constraints and multi-physics FFF simulation results into a deep neural network (DNN), thus ensuring consistency with physical laws: (1) incorporate physics constraints within the loss function of the DNN, (2) use physics model outputs as additional inputs to the DNN model, and (3) pre-train a DNN model with physics model input-output and then update it with experimental data. These strategies help to enforce a physically consistent relationship between bond quality and tensile strength, thus making porosity predictions physically meaningful. Eight different combinations of the above strategies are investigated. The results show how the combination of multiple strategies produces accurate machine learning models even with limited experimental data.

Reliable prediction of crystallographic texture in laser powder bed fusion is critical for linking process conditions with anisotropic response and for qualification. However, black-box models may fail under shift and cannot distinguish weak data support from loss of physical validity. This study develops a two-stage physics-based model for <001> || BD (build direction) texture in Inconel 718. Stage 1 maps process variables to melting mode and melt pool geometry. Stage 2 predicts texture by combining an empirical physics model with a random-forest residual model. A k-nearest-neighbor weight attenuates residual corrections for poorly supported queries, while a study-specific areal beam-power-density criterion withholds predictions outside the adopted conduction envelope. Conformal intervals are evaluated on the retained physics-valid set, and SHAP and Sobol analyses assess residual sensitivity. Under a controlled leave-one-defocus-out evaluation, the physics anchor achieved R^2 = 0.778, against -0.001 for the black-box model and 0.750 for the gated hybrid. Under leave-one-group-out cross-validation, the gated hybrid reached R^2 = 0.592 against 0.538 for the black-box model. Retained-set coverage was 92.9% at a mean full width of 3.65 multiples of a uniform distribution (MUD) under grouped cross-validation and 100% at a width of 3.21 MUD under transfer to a withheld +80 mm defocus regime. An illustrative mapping produced a retained BD elastic-modulus span of 127-187 GPa. On nine conditions from a separately built sample set, the framework withheld three, attenuated three, and matched the measured ordering for the rest. Separating data applicability, physics validity, and predictive uncertainty into distinct decisions lets the framework transfer where an unconstrained model does not, and withhold predictions where no model class performs adequately.